Dissolvable Bar

Our company can research and develop according to customers' technical requirements and downhole parameters, and process and produce dissolvable bars that can meet the operation requirements of our customers.

Back to list

Tel：18912982524

Category

Dissolvable Bars

Online message

Dissolvable Bar

Product description

HS-M100 Dissolvable Bar

Material

Magnesium Alloy

Density

1.8-1.9g/cm³

Tensile Strength

330Mpa

Yield Strength

230Mpa

Elongation

6-8%

Dissolution data

At 93℃, 3% KCL liquid, this material is processed into balls that dissolve with an average of 0.7mm in diameter per hour or 70mg/cm2/hr ( 93℃, 3%KCL )

In a 65℃, 3% KCL liquid, the material is processed into balls that dissolve with an average of 0.3mm in diameter per hour or 40mg/cm2/hr ( 65℃, 3%KCL )

Bar mould size

Φ60 Φ70 Φ80 Φ90 Φ100 Φ110 Φ120 Φ130

HS-M200 Dissolvable Bar

Material

Magnesium Alloy

Density

1.9-2.0g/cm³

Tensile Strength

420Mpa

Yield Strength

310Mpa

Elongation

5-6%

Dissolution data

At 93℃, 3% KCL liquid, this material is processed into balls, that dissolve with an average of 0.3mm in diameter per hour or 40mg/cm2/hr ( 93℃, 3%KCL )

At 65℃, 3% KCL liquid, this material is processed into balls that dissolve with an average of 0.15mm in diameter per hour or 20mg/cm2/hr ( 65℃, 3%KCL )

Bar mould size

Φ60 Φ70 Φ80 Φ90 Φ100 Φ110 Φ120 Φ130

HS-M300 Dissolvable Bar

Material

Magnesium Alloy

Density

1.8-1.9g/cm³

Tensile Strength

280Mpa

Yield Strength

190Mpa

Elongation

11-15%

Dissolution data

At 93℃, 3% KCL liquid, this material is processed into balls that dissolve with an average of 0.3mm in diameter per hour or 40mg/cm2/hr ( 93℃, 3%KCL )

Bar mould size

Φ60 Φ70 Φ80 Φ90 Φ100 Φ110 Φ120 Φ130

HS-M400 Dissolvable Bar

Material

Magnesium Alloy

Density

1.8-1.9g/cm³

Tensile Strength

200Mpa

Yield Strength

150Mpa

Elongation

40%

Dissolution data

At 93℃, 3% KCL liquid, this material is processed into balls with an average diameter of 0.1mm per hour or 20mg/cm2/hr ( 93℃, 3%KCL )

Bar mould size

Φ60 Φ70 Φ80 Φ90 Φ100 Φ110 Φ120 Φ130

HS-M500 Dissolvable Bar

Material

Magnesium Alloy

Density

1.8-1.9g/cm³

Tensile Strength

240Mpa

Yield Strength

190Mpa

Elongation

11-15%

Dissolution data

In a 93℃, 3% KCL liquid, this material is processed into balls that dissolve with an average of 1.5mm in diameter per hour or150mg/cm2/hr ( 93℃, 3%KCL )

At 65℃, 3% KCL liquid, this material is processed into ball that dissolve with an average of 0.4mm in diameter per hour or 40mg/cm2/hr (65℃, 3%KCL)

Bar mould size

Φ60 Φ70 Φ80 Φ90 Φ100 Φ110 Φ120 Φ130

HS-M600 Dissolvable Bar

Material

Magnesium Alloy

Density

1.8-1.9g/cm³

Tensile Strength

260Mpa

Yield Strength

220Mpa

Elongation

8-10%

Dissolution data

At 93℃, 3% KCL liquid, this material is processed into balls and dissolves an average of 2.8mm in diameter per hour or 280mg/cm2/hr ( 93℃, 3%KCL )

At 65℃, 3% KCL liquid, this material is processed into balls thatdissolve with an average of 1.4mm in diameter per hour. or 140mg/cm2/hr ( 65℃, 3%KCL)

At 93℃, in clear water, the material is processed into balls that dissolve with an average of 0.2mm in diameter per hour. or 30mg/cm2/hr ( 93℃, freshwater )

Bar mould size

Φ60 Φ70 Φ80 Φ90 Φ100 Φ110 Φ120 Φ130

HS-M700 Dissolvable Bar

Material

Magnesium Alloy

Density

1.8-1.9g/cm³

Tensile Strength

300Mpa

Yield Strength

260Mpa

Elongation

5-6%

Dissolution data

In a 93℃, 3% KCL liquid, this material is processed into balls that dissolve with an average of 3.5mm in diameter per hour or 350mg/cm2/hr ( 93℃, 3%KCL )

In a 65℃, 3% KCL liquid, the material was processed into balls, dissolving an average of 2.3mm in diameter per hour or 230mg/cm2/hr ( 65℃℉, 3%KCL)

At 93℃, in clear water, the material is processed into balls that dissolve with an average of 0.4mm in diameter per hour or 50mg/cm2/hr ( 93℃, freshwater )

Bar mould size

Φ60 Φ70 Φ80 Φ90 Φ100 Φ110 Φ120 Φ130